Hostaform® LX90

聚甲醛（POM）共聚物

Celanese Corporation

Technical Data

 

产品说明

 

Preliminary Data Sheet

 

Hostaform® LX90 specialty metallic appearance grades are an integrally colored nominal 9 melt flow rate based acetal copolymer material formulated to provide an exceptional molded in metallic appearance. This product is available in many metallic molded-in-colors.

 

Besides material, optimal finish for specialty metallic parts is dependent on proper drying, gate design, knit line locations, and special processing. Please contact Celanese Technical Service for assistance with your application.

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Technical Datasheet - ISO (English)

 

搜索 UL 黄卡 •  Celanese Corporation

•  Hostaform®

供货地区 • 北美洲 • 欧洲

特性 • 通用

用途 • 通用

RoHS 合规性 • 联系制造商

外观 • 金属化 - 染色 • 可用颜色

 

物理性能 额定值单位制 测试方法

密度 1.43g/cm³ ISO 1183

溶化体积流率（MVR） (190°C/2.16 kg) 8.00cm³/10min ISO 1133

吸水率 (饱和, 23°C) 0.75% ISO 62

机械性能 额定值单位制 测试方法

拉伸模量 2700MPa ISO 527-2/1A/1

拉伸应力 (屈服) 56.0MPa ISO 527-2/1A/50

拉伸应变 (屈服) 10% ISO 527-2/1A/50

弯曲模量 (23°C) 2700MPa ISO 178

冲击性能 额定值单位制 测试方法

简支梁缺口冲击强度 ISO 179/1eA

-30°C 4.0kJ/m²

23°C 5.0kJ/m²

热性能 额定值单位制 测试方法

热变形温度 (1.8 MPa, 未退火) 88.0°C ISO 75-2/A

熔融温度 3 166°C ISO 11357-3

注射 额定值单位制

干燥温度 105 到 110°C

干燥时间 3.0hr

料筒后部温度 170 到 175°C

料筒中部温度 170 到 180°C

料筒前部温度 175 到 185°C

射嘴温度 185 到 195°C

加工（熔体）温度 180 到 195°C

模具温度 80.0 到 105°C

注塑压力 60.0 到 120MPa

注射速度 慢

保压 60.0 到 120MPa

背压 0.00 到 0.500MPa

 

 

Hostaform® LX90

聚甲醛（POM）共聚物

Celanese Corporation

 

注射说明

Manifold Temperature: 180 to 200°C

Zone 4 Temperature: 180 to 190°C

 

 

 

 

 

 

 