Radici Compounds AH50P
乙缩醛（POM）均聚物
Radici Plastics USA, Inc.
Technical Data
产品说明
AH50P is an acetal homopolymer, with a viscosity suitable for general-purpose injection molding applications; it is formulated to offer improved melt stability, and is internally lubricated for ease of mold release.
Acetal homopolymer is a highly crystalline engineering thermoplastic polymer exhibiting predictable mechanical properties over a wide temperature range and for long time periods. A combination of high tensile strength and rigidity, resilience and toughness, outstanding dynamic and static fatigue resistance, excellent dimensional stability, resistance to the effects of a wide range of chemicals, oils and solvents and natural lubricity makes acetal homopolymer the material of choice for a wide range of applications in all major end-use categories.
总体
材料状态 • 已商用：当前有效
资料 1 • Technical Datasheet (English)
Search for UL Yellow Card • Radici Plastics USA, Inc.
供货地区 • 北美洲
添加剂 • 脱模
• 尺寸稳定性良好 • 均聚物 • 耐油性能
• 刚性，高 • 抗溶解性
性能特点 • 韧性良好
• 高拉伸强度 • 耐化学性良好
• 有弹性
• 结晶 • 耐疲劳性能
形式 • 颗粒料
加工方法 • 注射成型
物理性能 额定值单位制 测试方法
比重 1.42g/cm³ ASTM D792
收缩率 - 流动 (3.18 mm) 2.0 到 2.4% ASTM D955
吸水率 (24 hr) 0.25% ASTM D570
机械性能 额定值单位制 测试方法
抗张强度 (屈服) 72.4MPa ASTM D638
伸长率 (断裂) 25 到 35% ASTM D638
弯曲模量 2900MPa ASTM D790
弯曲强度 102MPa ASTM D790
摩擦系数 ASTM D1894
与金属 - 动态 0.20
与金属 - 静态 0.13
冲击性能 额定值单位制 测试方法
悬壁梁缺口冲击强度 (23°C, 3.18 mm) 85 到 96J/m ASTM D256
硬度 额定值单位制 测试方法
洛氏硬度 (R 计秤) 120 ASTM D785
热性能 额定值单位制 测试方法
热变形温度 (1.8 MPa, 未退火) 135°C ASTM D648
熔融温度 170 到 175°C ASTM D789
注射 额定值单位制
干燥温度 76.7 到 87.8°C
干燥时间 1.0 到 2.0hr
建议注入量 40 到 70%
螺筒后部温度 199°C
螺筒中部温度 204°C
螺筒前部温度 210°C
加工（熔体）温度 204 到 216°C
模具温度 82.2 到 116°C
背压 0.345MPa
1 / 3 文件号： TDS-64590-zh
应商进行验证。
Radici Compounds AH50P
乙缩醛（POM）均聚物
Radici Plastics USA, Inc.
注射 额定值单位制
螺杆转速 40 到 80rpm
垫层 3.18 到 6.35mm
备注
1 通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料；不过您可以从供应商处了解最新资料。
2 一般属性：这些不能被视为规格。
|