Kareline® POMS6040
乙缩醛（POM）均聚物

Kareline Oy Ltd.  
    
 Technical Data   
    

产品说明

The matrix plastic of Kareline® POMS is co-polyacetal (POM). The fibre used is ECF bleached long fibre Nordic soft wood pulp (cellulose). The fibre content of Kareline® POMS composites is 10 - 40 weight% (for example Kareline® POMS6040, Kareline® POMS7030). Customers made grades are also available.

Kareline® POMS composites have a lot of good properties:  
• High rigidity    
• Good impact strength as natural fibre composite  
• Excellent abrasion resistance    
• Good chemical and stress cracking resistance  
• Easy to machine    
• Low friction surfaces    
• Small shrinkages in injection moulding   
• Dimensional stability and absence of shrink marks  
总体     
材料状态 • 已商用：当前有效  
资料 1 •  Technical Datasheet (English)
 
供货地区 • 欧洲  
填料/增强材料 • 木纤维, 50% 填料按重量  
  • 超声波可焊接 • 可更新资源 • 耐磨蚀性，良好
  • 尺寸稳定性良好 • 可切削 • 耐气候影响性能良好
性能特点 • 低摩擦系数 • 良好的表面光洁度 • 热绝缘
  • 刚性，高 • 良好的着色性 • 柔软
  • 抗撞击性，良好 • 耐化学性良好 • 适于粉刷
外观  • 自然色  
形式  • 颗粒料  
加工方法 • 注射成型  
    
物理性能   额定值单位制 测试方法
密度    1.42g/cm³ ISO 1183
溶化体积流率（MVR） (200°C/10.0 kg)   14.8cm³/10min ISO 1133
收缩率   1.3% 
机械性能   额定值单位制 测试方法
拉伸模量   4300MPa ISO 527-2
拉伸应力 (屈服)   74.1MPa ISO 527-2
拉伸应变 (屈服)   3.1% ISO 527-2
弯曲模量   6500MPa ISO 178
Tensile Strength/Weight Ratio   52.0MPa/g/cm³ 
冲击性能   额定值单位制 测试方法
简支梁缺口冲击强度 (23°C)   2.3kJ/m² ISO 179
硬度    额定值单位制 测试方法
支撐硬度 (邵氏 D, 23°C)   83 ISO 868
热性能    额定值单位制 
最高连续使用温度   -40.0 到 110°C 
     
注射    额定值单位制 
干燥温度   80.0 到 100°C 
干燥时间   4.0 到 8.0hr 
螺筒后部温度   200°C 
螺筒中部温度   195°C 
螺筒前部温度   190°C 
射嘴温度   180°C 

1 / 3 文件号： TDS-120538-zh
 
 
 
 
 
 
Kareline® POMS6040
乙缩醛（POM）均聚物
Kareline Oy Ltd.  
     
  注射 额定值单位制 
    
  加工（熔体）温度 < 210°C 
  模具温度 20.0 到 60.0°C 
  注塑温度 < 100MPa 
  注射说明   
  Nozzle Diameter: >4mm   

备注